In this paper the effects of post deposition heat treatments on the cohesive and adhesive strength properties of PS304, a plasma sprayed nickel-chrome based, high temperature solid lubricant coating deposited on stainless steel, are studied. Plasma spray deposited coating samples were exposed in air at temperatures from 432 to 650 C for up to 500 hr to promote residual stress relief, enhance particle to particle bonding and increase coating to substrate bond strength. Coating pull-off strength was measured using a commercial adhesion tester that utilizes 13 mm diameter aluminum pull studs attached to the coating surface with epoxy. Pull off force was automatically recorded and converted to coating pull off strength. As deposited coating samples were also tested as a baseline. The as-deposited (untreated) samples either delaminated at the coating-substrate interface or failed internally (cohesive failure) at about 17 MPa. Samples heat treated at temperatures above 540 C for 100 hr or at 600 C or above for more than 24 hr exhibited strengths above 31 MPa, nearly a two fold increase. Coating failure occurred inside the body of the coating (cohesive failure) for nearly all of the heat-treated samples and only occasionally at the coating substrate interface (adhesive failure). Metallographic analyses of heat-treated coatings indicate that the Nickel-Chromium binder in the PS304 appears to have segregated into two phases, a high nickel matrix phase and a high chromium precipitated phase. Analysis of the precipitates indicates the presence of silicon, a constituent of a flow enhancing additive in the commercial NiCr powder. The exact nature and structure of the precipitate phase is not known. This microstructural change is believed to be partially responsible for the coating strength increase. Diffusion bonding between particles may also be playing a role. Increasing the heat treatment temperature, exposure time or both accelerate the heat treatment process. Preliminary me...

Since the publication of the best-selling first edition, the growing price and environmental cost of energy have increased the significance of tribology. Handbook of Lubrication and Tribology, Volume II: Theory and Design, Second Edition demonstrates how the principles of tribology can address cost savings, energy conservation, and environmental protection. This second edition provides a thorough treatment of established knowledge and practices, along with detailed references for further study. Written by the foremost experts in the field, the book is divided into four sections. The first reviews the basic principles of tribology, wear mechanisms, and modes of lubrication. The second section covers the full range of lubricants/coolants, including mineral oil, synthetic fluids, and water-based fluids. In the third section, the contributors describe many wear- and friction-reducing materials and treatments, which are currently the fastest growing areas of tribology, with announcements of new coatings, better performance, and new vendors being made every month. The final section presents components, equipment, and designs commonly found in tribological systems. It also examines specific industrial areas and their processes. Sponsored by the Society of Tribologists and Lubrication Engineers, this handbook incorporates up-to-date, peer-reviewed information for tackling tribological problems and improving lubricants and tribological systems. The book shows how the proper use of generally accepted tribological practices can save money, conserve energy, and protect the environment.

Since the publication of the best-selling first edition, the growing price and environmental cost of energy have increased the significance of tribology. Handbook of Lubrication and Tribology, Volume II: Theory and Design, Second Edition demonstrates how the principles of tribology can address cost savings, energy conservation, and environmental pr