Provides general descriptions of degradation mechanisms of different types of stress corrosion cracking (SCC) which are concerned with systems, structures and components in PWRs and BWRs. This publication includes examples of good practices in preventing, mitigating and repairing SCC damage and summarizes research and development programmes.

Stress corrosion cracking is a major problem in light water nuclear reactors, whether pressurised water reactors (PWRs) or boiling water reactors (BWRs). The nuclear industry needs to be able to predict the service life of these power plants and develop appropriate maintenance and repair practices to ensure safe long term operation. This important book sums up key recent research on corrosion in light water reactors and its practical applications.The book is divided into four parts. It begins with an overview of materials degradation due to stress corrosion, corrosion potential monitoring and passivation. Part two summarises research on susceptibility of materials to stress corrosion cracking and the ways it can be initiated. The third part of the book considers stress corrosion crack propagation processes whilst the final part includes practical case studies of corrosion in particular plants. The book reviews corrosion in a range of materials such as low alloy steels, stainless steels and nickel-based alloys.With its distinguished editor and team of contributors, Corrosion issues in light water reactors is a standard work for the nuclear industry. - Summarises key recent research on corrosion in light water reactors - Includes practical case studies

Nuclear Corrosion: Research, Progress and Challenges, part of the "Green Book” series of the EFC, builds upon the foundations of the very first book published in this series in 1989 ("Number 1 - Corrosion in the Nuclear Industry”). This newest volume provides an overview on state-of-the-art research in some of the most important areas of nuclear corrosion. Chapters covered include aging phenomena in light water reactors, reprocessing plants, nuclear waste disposal, and supercritical water and liquid metal systems. This book will be a vital resource for both researchers and engineers working within the nuclear field in both academic and industrial environments.

High-performance alloys that can withstand operation in hazardous nuclear environments are critical to presentday in-service reactor support and maintenance and are foundational for reactor concepts of the future. With commercial nuclear energy vendors and operators facing the retirement of staff during the coming decades, much of the scholarly knowledge of nuclear materials pursuant to appropriate, impactful, and safe usage is at risk. Led by the multi-award winning editorial team of G. Robert Odette (UCSB) and Steven J. Zinkle (UTK/ORNL) and with contributions from leaders of each alloy discipline, Structural Alloys for Nuclear Energy Applications aids the next generation of researchers and industry staff developing and maintaining steels, nickel-base alloys, zirconium alloys, and other structural alloys in nuclear energy applications. This authoritative reference is a critical acquisition for institutions and individuals seeking state-of-the-art knowledge aided by the editors' unique personal insight from decades of frontline research, engineering and management. - Focuses on in-service irradiation, thermal, mechanical, and chemical performance capabilities. - Covers the use of steels and other structural alloys in current fission technology, leading edge Generation-IV fission reactors, and future fusion power reactors. - Provides a critical and comprehensive review of the state-of-the-art experimental knowledge base of reactor materials, for applications ranging from engineering safety and lifetime assessments to supporting the development of advanced computational models.

Stress corrosion cracking is a major problem in light water nuclear reactors, whether pressurised water reactors (PWRs) or boiling water reactors (BWRs). The nuclear industry needs to be able to predict the service life of these power plants and develop appropriate maintenance and repair practices to ensure safe long term operation. This important book sums up key recent research on corrosion in light water reactors and its practical applications. The book is divided into four parts. It begins with an overview of materials degradation due to stress corrosion, corrosion potential monitoring and passivation. Part two summarises research on susceptibility of materials to stress corrosion cracking and the ways it can be initiated. The third part of the book considers stress corrosion crack propagation processes whilst the final part includes practical case studies of corrosion in particular plants. The book reviews corrosion in a range of materials such as low alloy steels, stainless steels and nickel-based alloys. With its distinguished editor and team of contributors, Corrosion issues in light water reactors is a standard work for the nuclear industry. Summarises key recent research on corrosion in light water reactorsIncludes practical case studies.

Accident Tolerant Materials for Light Water Reactor Fuels provides a description of what an accident tolerant fuel is and the benefits and detriments of each concept. The book begins with an introduction to nuclear power as a renewable energy source and the current materials being utilized in light water reactors. It then moves on to discuss the recent advancements being made in accident tolerant fuels, reviewing the specific materials, their fabrication and implementation, environmental resistance, irradiation behavior, and licensing requirements. The book concludes with a look to the future of new power generation technologies. It is written for scientists and engineers working in the nuclear power industry and is the first comprehensive work on this topic. - Introduces the fundamental description of accident tolerant fuel, including fabrication and implementation - Describes both the benefits and detriments of the various Accident Tolerant Fuel concepts - Includes information on the process of materials selection with a discussion of how and why specific materials were chosen, as well as why others failed

Corrosion of nuclear materials, i.e. the interaction between these materials and their environments, is a major issue for plant safety as well as for operation and economic competitiveness. Understanding these corrosion mechanisms, the systems and materials they affect, and the methods to accurately measure their incidence is of critical importance to the nuclear industry. Combining assessment techniques and analytical models into this understanding allows operators to predict the service life of corrosion-affected nuclear plant materials, and to apply the most appropriate maintenance and mitigation options to ensure safe long term operation.This book critically reviews the fundamental corrosion mechanisms that affect nuclear power plants and facilities. Initial sections introduce the complex field of nuclear corrosion science, with detailed chapters on the different types of both aqueous and non aqueous corrosion mechanisms and the nuclear materials susceptible to attack from them. This is complemented by reviews of monitoring and control methodologies, as well as modelling and lifetime prediction approaches. Given that corrosion is an applied science, the final sections review corrosion issues across the range of current and next-generation nuclear reactors, and across such nuclear applications as fuel reprocessing facilities, radioactive waste storage and geological disposal systems.With its distinguished editor and international team of expert contributors, Nuclear corrosion science and engineering is an invaluable reference for nuclear metallurgists, materials scientists and engineers, as well as nuclear facility operators, regulators and consultants, and researchers and academics in this field. - Comprehensively reviews the fundamental corrosion mechanisms that affect nuclear power plants and facilities - Chapters assess different types of both aqueous and non aqueous corrosion mechanisms and the nuclear materials susceptible to attack from them - Considers monitoring and control methodologies, as well as modelling and lifetime prediction approaches