Badeker in 1907 observed that some materials are optically transparent in the visible light and electrically conducting [1]. Because of the increasing interest in electrically and electronically active materials, the search for materials and the techniques for producing semi-transparent electrically conducting films have gained much importance. In an intrinsic stoichiometric material, it is not possible to have simultaneously high transparency (>80%%) in the visible region and high electrical conductivity (>103 Ω cm-1). A variety of metals in thin film form (

This project provided a proof-of-concept that indium tin oxide (ITO) thin films can be prepared on surfaces by pulsed laser deposition and configured as miniature strain gauges. The degree of piezoresistivity of the films is related to the oxygen content, with larger gauge factors correlated with oxygen excess. Typical gauge factors of order 10 were observed. Gauges as small as 20x 100 microns were fabricated by focused ion beam milling and characterized. Radiation effects from ion beam milling were observed and measured. Structures encapsulated with silicon dioxide protective films retailed their piezoresistive coefficient and were less susceptible to damage by focused ion beam imaging.

This dissertation, "Preparation and Post-annealing Effects on the Optical Properties of Indium Tin Oxide Thin Films" by Rongxin, Wang, 王榮新, was obtained from The University of Hong Kong (Pokfulam, Hong Kong) and is being sold pursuant to Creative Commons: Attribution 3.0 Hong Kong License. The content of this dissertation has not been altered in any way. We have altered the formatting in order to facilitate the ease of printing and reading of the dissertation. All rights not granted by the above license are retained by the author. Abstract: Abstract of thesis entitled PREPARATION AND POST-ANNEALING EFFECTS ON THE OPTICAL PROPERTIES OF INDIUM TIN OXIDE THIN FILMS Submitted by WANG Rong Xin for the degree of Doctor of Philosophy at The University of Hong Kong in April 2005 Many opto-electronic devices, such as III-V compound devices, liquid crystal displays, solar cells, organic and inorganic light emitting devices, and ultraviolet photodetectors, demand transparent electrode materials simultaneously having high electrical conductance. To meet the requirements for particular applications, a great deal of basic research and studies have been carried out on the electrical and optical properties of these materials. As a most promising candidate for such materials, indium tin oxide (ITO) has attracted interest in recent years. Furthermore, ITO has many unique properties such as excellent adhesion on the substrate, thermal stability and ease of patterning. The deposition of high-quality ITO thin films is a key step for successful application of ITO thin films as transparent electrode materials. To obtain optimal electrical and optical properties of ITO films, the growth parameters and conditions must be determined. Moreover, the optical and electrical properties of ITO contact layers, which can either be on the top side or the bottom side of a device, are influenced by various post-deposition treatments. For the present work, ITO thin films were deposited on glass and quartz substrates using e-beam evaporation with different deposition rates. The influence of substrate material, deposition rate, deposition gas environment and post-deposition annealing on the optical properties of the films was investigated in detail. Atomic force microscopy, X-ray diffraction and X-ray photoemission spectroscopy was employed to obtain information on the chemical state and crystallization of the films. Analysis of these data suggests that the substrate material, deposition rate, deposition gas environment and post-deposition annealing conditions strongly affect the chemical composition and the microstructure of the ITO films and these in turn influence the optical properties of the film. Oxygen incorporation transfers the In O phase to the In O phase and removes metallic In to form both indium oxide 2 3-x 2 3 phases. Both of these reactions are beneficial for the optical transmittance of ITO thin films. Moreover, it was found that the incorporation and decomposition reactions of oxygen can be controlled so as to change the optical properties of the ITO thin films reversibly. DOI: 10.5353/th_b3154617 Subjects: Thin films - Optical properties Indium compounds Annealing of metals