Concrete corrosion induced by deicing agents can decrease the durability of concrete bridge decks by causing cross-sectional loss of reinforcement, concrete delamination, and spalling owing to the expansion of corroded reinforcement. The installation of overlays can extend the service life of the deteriorated decks. However, overlays present challenges in the evaluation of the corrosion condition of the underlying decks. This laboratory study employed three nondestructive testing (NDT) methods to assess the effects of seven types of overlays on corrosion evaluation for concrete bridge decks. The NDT methods were electrical resistivity (ER), ground-penetrating radar (GPR), and half-cell potential (HCP). The ER method could not evaluate the corrosive environment in the concrete decks through the overlays. The GPR method could detect the corrosive environment through four of the seven overlays. The HCP method could detect the decrease of electrical potential over the actively corroded reinforcement for all seven specimens; however, only two of the seven specimens could be identified as having active corrosion per ASTM C876-15, Standard Test Method for Corrosion Potentials of Uncoated Reinforcing Steel in Concrete . Overlay debonding did not affect GPR and HCP testing results in this study.

Corrosion of reinforcing steel is now recognized as the major cause of degradation of concrete structures in many parts of the world. Despite this, infrastructure expenditure is being unreasonably decreased by sequestration and the incredible shrinking discretionary budget. All components of our infrastructure including highways, airports, water supply, waste treatment, energy supply, and power generation require significant investment and are subjected to degradation by corrosion, which significantly reduces the service life, reliability, functionality of structures and equipment, and safety. Corrosion of Steel in Concrete Structures provides a comprehensive review of the subject, in addition to recent advances in research and technological developments, from reinforcing materials to measurement techniques and modelling. This book contains not only all the important aspects in the field of corrosion of steel reinforced concrete but also discusses new topics and future trends. Part One of the book tackles theoretical concepts of corrosion of steel in concrete structures. The second part moves on to analyse the variety of reinforcing materials and concrete, including stainless steel and galvanized steel. Part Three covers measurements and evaluations, such as electrochemical techniques and acoustic emission. Part Four reviews protection and maintenance methods, whilst the final section analyses modelling, latest developments and future trends in the field. The book is essential reading for researchers, practitioners and engineers who are involved in materials characterisation and corrosion of steel in concrete structures. Provides comprehensive coverage on a broad range of topics related to the corrosion of steel bars in concrete Discusses the latest measuring methods and advanced modeling techniques Reviews the range of reinforcing materials and types of concrete

Corrosion of Steel in Concrete: Understanding, Investigation and Repair is a guide for designing, constructing and maintaining reinforced concrete structures, such as buildings and bridges which are subject to reinforcement corrosion. It presents the basics of theory and practice in steel corrosion in concrete and reviews the latest research and developments, such as progress on measuring the corrosion threshold for chloride-induced corrosion. This third edition compares the currently proliferating major national and international standards and guidance documents. New developments are considered, such as hybrid anodes for electrochemical treatment and the latest research and developments in assessment, such as the use of ground penetrating radar to measure the chloride content of the concrete cover. It overhauls coverage of electrochemical repair and rehabilitation techniques and outlines recent innovations in structural repair and construction and investigates their implications for durability. The book is ideal for practitioners and graduate students in structural engineering and concrete technology.

The proposed study explores the feasibility of detecting and quantifying corrosion and delamination (physical separation) at the interface between reinforcing steel bars and concrete using ultrasonic guided waves. The problem of corrosion of the reinforcing steel in structures has increased significantly in recent years. The emergence of this type of concrete deterioration, which was first observed in marine structures and chemical manufacturing plants, coincided with the increased applications of deicing salts (sodium and calcium chlorides) to roads and bridges during winter months in those states where ice and snow are of major concern. Concrete is strengthened by the inclusion of the reinforcement steel such as deformed or corrugated steel bars. Bonding between the two materials plays a vital role in maximizing performance capacity of the structural members. Durability of the structure is of concern when it is exposed to aggressive environments. Corrosion of reinforcing steel has led to premature deterioration of many concrete members before their design life is attained. It is therefore, important to be able to detect and measure the level of corrosion in reinforcing steel or delamination at the interface. The development and implementation of damage detection strategies, and the continuous health assessment of concrete structures then become a matter of utmost importance. The ultimate goal of this research is to develop a nondestructive testing technique to quantify the amount of corrosion in the reinforcing steel. The guided mechanical wave approach has been explored towards the development of such methodology. The use of an embedded ultrasonic network for monitoring corrosion in real structures is feasible due to its simplicity. The ultrasonic waves, specifically cylindrical guided waves can propagate a long distance along the reinforcing steel bars and are found to be sensitive to the interface conditions between steel bars and concrete. Ultrasonic transducers are used to launch and detect cylindrical guided waves along the steel bar. In this dissertation, in-situ corrosion monitoring technique for reinforced concrete is developed based on two methods - 1) variation of signal strength and 2) the time-of-flight (TOF) variations as the corroded member is loaded transversely. This is the first attempt ever to monitor corrosion inside concrete by measuring the change in the time of flight of guided waves along reinforcing bars as the concrete beam is subjected to bending. Advantages of corrosion monitoring by TOF change are discussed in the dissertation.