LA TENUE DES MOTEURS D'AVIONS PASSE DE PLUS EN PLUS PAR LES ANALYSES DE DUREES DE VIE SOUS SOLLICITATIONS DE SERVICE, FAISANT INTERVENIR, EN PARTICULIER, LES PHENOMENES DUS AUX TEMPERATURES ELEVEES. UNE NOUVELLE LOI DE PROPAGATION DES FISSURES EST ELABOREE, AVEC POUR OBJECTIF LES ANALYSES SYSTEMATIQUES DES DISQUES DE TURBINE. ELLE EST DETERMINEE ET UTILISEE SUR UN ALLIAGE POUR DISQUES, L'ASTROLOY (METALLURGIE DES POUDRES), A 650C. CETTE LOI A CARACTERE PHENOMENOLOGIQUE EST CONSTRUITE EN CHERCHANT A RENDRE COHERENTES DES OBSERVATIONS DE NATURES DIFFERENTES (EXPERIMENTALE, NUMERIQUE ET PHYSIQUE). EN PARTICULIER, ELLE S'APPUIE SUR: 1) UN VASTE PROGRAMME EXPERIMENTAL, MENE EN CONCERTATION ENTRE L'ONERA, L'ENSMP ET LA SNECMA, QUI A PERMIS, ENTRE AUTRES, DE METTRE EN EVIDENCE LES EFFETS DES TEMPS DE MAINTIEN A HAUTE TEMPERATURE, 2) UN ENSEMBLE DE SIMULATIONS NUMERIQUES MENEES EN VISCOPLASTICITE CYCLIQUE AVEC UN CODE D'ELEMENTS FINIS. LES PHENOMENES D'OUVERTURE-FERMETURE ET DE REDISTRIBUTIONS DE CONTRAINTES SONT ETUDIES EN DETAIL EN FONCTION DE LA PROPAGATION DE LA FISSURE (METHODE DE RELACHEMENT DES NUDS), 3) DES OBSERVATIONS FAITES PAR AILLEURS SUR LES CINETIQUES D'OXYDATION ET LEUR INFLUENCE SUR LA FRAGILISATION DU MATERIAU. UN MODELE DE PROPAGATION EST AINSI ELABORE DANS LE CADRE DE LA MECANIQUE LINEAIRE DE LA RUPTURE, EN COMBINANT PROPAGATION PAR FATIGUE ET PAR FLUAGE, EFFET MECANIQUE DE RELAXATION DU SEUIL DE NON-PROPAGATION ET EFFET DE FRAGILISATION PAR OXYDATION EN TETE DE FISSURE. IL PERMET DE TRADUIRE FIDELEMENT LA PROPAGATION SOUS DES CYCLES DE CHARGEMENT DE FORME COMPLEXE, FAISANT INTERVENIR DES PHASES DE MAINTIEN AU COURS DES TRANSITOIRES DE DECHARGE

CETTE ETUDE PORTE SUR LE COMPORTEMENT EN FISSURATION A 750\C DE SUPERALLIAGES A BASE DE NICKEL POUR DISQUES DE TURBINE. CES ALLIAGES AVAIENT SURTOUT ETE AMPLEMENT ETUDIES JUSQU'AUX TEMPERATURES DE 600-650\C MAIS LE DEVELOPPEMENT DES NOUVEAUX MOTEURS NECESSITE UNE MEILLEURE COMPREHENSION DES INTERACTIONS POSSIBLES ENTRE LES DIFFERENTS FACTEURS QUE SONT LA FATIGUE, LE FLUAGE ET L'OXYDATION QUI GOUVERNENT L'ENDOMMAGEMENT AUX PLUS HAUTES TEMPERATURES. A 750\C, LE MODE DE FISSURATION INTERGRANULAIRE ENTRAINE UNE FORTE SENSIBILITE DES ALLIAGES AUX PARAMETRES MICROSTRUCTURAUX. UNE ETUDE DE FOND A ETE CONDUITE SUR LES INTERACTIONS FATIGUE-FLUAGE SUR UNE MICROSTRUCTURE DE REFERENCE D'UN ALLIAGE : L'ASTROLOY ATGP3. LES TENDANCES OBSERVEES ONT ETE VALIDEES SUR D'AUTRES MICROSTRUCTURES DE CE MATERIAU OU SUR D'AUTRES ALLIAGES : LE N18 OU SUR LE NR3 RECEMMENT DEVELOPPE PAR L'ONERA. L'ETUDE A ETE ABORDEE EN DECOUPLANT LES EFFETS DE FLUAGE ET D'OXYDATION, TOUS DEUX THERMIQUEMENT ACTIVES, PAR UNE CARACTERISATION EN FATIGUE-FLUAGE SOUS VIDE. LA METHODE EXPERIMENTALE MISE AU POINT, BASEE SUR LE SUIVI ELECTRIQUE DE LA FISSURE, A PERMIS DE DISTINGUER LA PROPAGATION A CHAQUE REMISE EN CHARGE DE CELLE SURVENANT PENDANT LE PALIER POUR LES SPECTRES DE CHARGEMENT TRAPEZOIDAUX APPLIQUES. DES INTERACTIONS ENTRE L'ENDOMMAGEMENT CYCLIQUE ET STATIQUE ONT AINSI PU ETRE IDENTIFIEES ET QUANTIFIEES POUR ABOUTIR A UN MODELE PHENOMENOLOGIQUE DE PROPAGATION QUI INTEGRE LES PARAMETRES DE FISSURATION QUE SONT LA FORME DU SPECTRE DE CHARGEMENT ET LE FACTEUR D'INTENSITE DE CONTRAINTE. PAR AILLEURS, DES ESSAIS SOUS AIR ONT ETE CONDUITS POUR PERMETTRE D'IDENTIFIER LES EFFETS COMPLEXES DE L'ENVIRONNEMENT A 750\C. L'EVOLUTION DE LA PRECIPITATION GAMMA PRIME INTRAGRANULAIRE

RECHERCHE D'UN PARAMETRE DE CHARGEMENT SUSCEPTIBLE DE REPRESENTER CORRECTEMENT LA PROPAGATION DE FISSURES A HAUTE TEMPERATURE. DANS CE CAS, LE FACTEUR D'INTENSITE DE CONTRAINTE K EST LE PARAMETRE QUI PERMET LES MEILLEURS CORRELATIONS ENTRE VITESSE DE PROPAGATION ET VARIABLES EXPERIMENTALES. ACTION DE L'OXYGENE SUR LA PROPAGATION. MODELISATION DE LA PROPAGATION EN FLUAGE ET FATIGUE-FLUAGE

CETTE ETUDE PORTE SUR LA PROPAGATION DE FISSURE A 650C DANS UN ACIER INOXYDABLE AUSTENITIQUE DE NUANCE Z2 CND 17-12. ELLE EST BASEE SUR TRAVAIL UN EXPERIMENTAL (37 ESSAIS) QUI CONCERNE, TOUT D'ABORD, DES EPROUVETTES DE TYPE CT SOLLICITEES A 650C EN FATIGUE, FLUAGE, FATIGUE-FLUAGE EN FORCE IMPOSEE. ENSUITE, DES TUBES FISSURES AVEC ENTAILLE CIRCONFERENTIELLE INTERNE SOLLICITES EN FLEXION 4 POINTS A DEPLACEMENT IMPOSE. EN UTILISANT LES OUTILS DE LA MECANIQUE DE LA RUPTURE (PARAMETRES K, J ET C*) ET DANS LE CADRE D'UNE APPROCHE GLOBALE DE LA PROPAGATION, IL S'AGIT ICI DE RECHERCHER UNE METHODOLOGIE DE CALCUL PERMETTANT DE PREVOIR L'EVOLUTION D'UNE FISSURE. LES OBSERVATIONS MICROSCOPIQUES ONT PERMIS D'IDENTIFIER DES FACIES DE RUPTURE TRANSGRANULAIRE OU MIXTE EN FATIGUE ET ESSENTIELLEMENT INTERGRANULAIRE EN FATIGUE-FLUAGE ET FLUAGE. EN FATIGUE CONTINUE, LA LOI DE PARIS DU MATERIAU A 650C RELIE LA VITESSE DE FISSURATION A LA VARIATION DU FACTEUR D'INTENSITE DES CONTRAINTES. EN FLUAGE PUR SUR EPROUVETTE CT, LA VITESSE PROPAGATION SUIT UNE CORRELATION QUI LA LIE A L'EVOLUTION DU PARAMETRE C* QUI PEUT ETRE ESTIME EXPERIMENTALEMENT, NUMERIQUEMENT ET ANALYTIQUEMENT. LES ESSAIS DE FATIGUE-FLUAGE AVEC TEMPS DE MAINTIEN COMPRIS ENTRE 1/2H ET 48H ONT MIS EN EVIDENCE UNE ACCELERATION SUR LA VITESSE DE FISSURATION PAR RAPPORT A LA LOI DE PARIS OBTENUE EN FATIGUE CONTINUE. POUR T#M 5H, LA VITESSE DIMINUE PUIS AUGMENTE A NOUVEAU ET SUIT UNE PENTE GLOBALEMENT PLUS RAIDE QUE LA LOI DE PARIS DU MATERIAU. CES EFFETS, ASSOCIES AUX OBSERVATIONS MICROSCOPIQUES, TRADUISENT L'INFLUENCE DES MECANISMES DE DEFORMATION ET DE LA LOI DE COMPORTEMENT DE FLUAGE SUR LA CINETIQUE DE FISSURATION. LA MODELISATION DES CES ESSAIS A PARTIR D'UN MODELE DE SOMMATION DES VITESSES DE FATIGUE ET DE FLUAGE FOURNI DES RESULTATS SATISFAISANTS QUAND LE PARAMETRE C* EST EVALUE A PARTIR DE L'ESTIMATION SIMPLIFIEE C*#S. POUR CELA, L'EVOLUTION DE L'ENDOMMAGEMENT DE FLUAGE AU COURS DE L'ESSAI DOIT ETRE PRISE EN COMPTE DANS LE CALCUL DES PARAMETRES ET DANS LEUR INTEGRATION.

CE TRAVAIL A POUR OBJET L'ETUDE DE LA FISSURATION A HAUTE TEMPERATURE D'UN SUPERALLIAGE DE LA METALLURGIE DES POUDRES A BASE DE NICKEL, L'ASTROLOY, UTILISE POUR LA FABRICATION DES DISQUES DE MOTEURS D'AVIONS. UNE ETUDE EXPERIMENTALE DE LA PROPAGATION DE FISSURES COURTES ET LONGUES SOUS CHARGEMENT DE FATIGUE, DE FATIGUE-FLUAGE ET DE FLUAGE A ETE EFFECTUEE SOUS AIR ET SOUS VIDE. ON MONTRE QU'UNE BAISSE DE FREQUENCE SOUS AIR CONDUIT A UNE FORTE ACCELERATION DES VITESSES DE FISSURATION, ELLE RESULTE PRINCIPALEMENT D'UNE ACTION DE L'ENVIRONNEMENT. A BASSE FREQUENCE SOUS AIR, L'EVOLUTION DA/DT-K#M#A#X, OBTENUE EN PRENANT UNE VITESSE MOYENNE DA/DT SUR LE CYCLE, EST IDENTIQUE A CELLE OBSERVEE EN FLUAGE PUR. NOUS AVONS IDENTIFIE LES CINETIQUES D'OXYDATION EN SURFACE ET PENETRANTE SUR EPROUVETTES LISSES. UN FORT COUPLAGE ENTRE LA CINETIQUE D'OXYDATION PENETRANTE ET UN CHARGEMENT IMPOSE A AINSI ETE QUANTIFIE. DES ESSAIS DE FISSURATION AVEC PREOXYDATION A HAUTE TEMPERATURE OU AVEC DES TRANSITOIRES DE CHARGEMENT A 650C, ONT MONTRE L'EXISTENCE D'UNE ZONE FRAGILISEE AU-DELA DE LA PENETRATION D'OXYDE. SUR LA BASE DE CES DONNEES EXPERIMENTALES, NOUS PROPOSONS DEUX CALCULS DE CROISSANCE DE FISSURE DISCONTINUE POUR MODELISER LES FORTES VITESSES DE FISSURATION SOUS AIR. DANS UN PREMIER MODELE, LA VITESSE DE FISSURATION RESULTE DE LA RUPTURE D'UN OXYDE FORME EN POINTE DE FISSURE. LA VITESSE DE FISSURATION EST DONC DEDUITE DE LA CINETIQUE D'OXYDATION COUPLEE AU CHARGEMENT EN POINTE DE FISSURE. LE SECOND MODELE EST UN EPUISEMENT DE DUCTILITE: LA FISSURE AVANCE SUR LA DISTANCE OU LE CHARGEMENT MECANIQUE DEPASSE LA DUCTILITE. L'HYPOTHESE D'UNE ACTION DEGRADANTE DE L'ENVIRONNEMENT AMPLIFIEE PAR UN CHARGEMENT A L'ORIGINE DES FORTES VITESSES DE FISSURATION OBSERVEES A BASSE FREQUENCE SOUS AIR EST CONFIRMEE PAR LE BON ACCORD ENTRE LES CALCULS ET L'EXPERIENCE

L’objectif de ce travail a tout d’abord été de développer une méthodologie de simulation numérique de propagation de fissure, en appliquant une approche couplée en chargement cyclique. On s’est intéressé, plus particulièrement, à l’utilisation d’éléments de zones cohésives couplés à une loi de comportement spécifique, afin de simuler, sans discontinuité, et avec un caractère prédictif, l’avancée d’une fissure. Enfin, nous avons établi un modèle phénoménologique de propagation, dans le cadre de la Mécanique Linéaire de la rupture, qui rend compte des effets de fissure courte et, à haute température, des effets de fluage et d’oxydation sur la vitesse de propagation par fatigue. L’objectif de ce modèle est de fournir aux Bureaux d’Etudes un outil rapide et facile à mettre en œuvre afin de dimensionner des pièces industrielles telles que les aubes de turbines. Cette étude, très riche en termes de résultats expérimentaux de propagation de fissure, a permis de développer une approche locale basée sur les modèles de zones cohésives pour la simulation numérique de la propagation de fissure. Mais les perspectives futures de l’application de telles méthodes sont de pouvoir fournir des informations sur le couplage complexe qui existe entre la plasticité en pointe de fissure et le phénomène de propagation qui permettront d’enrichir des modèles phénoménologiques applicables en Bureaux d’Etudes

CARACTERISATION EN FATIGUE OLIGOCYCLIQUE: L'ETUDE DETAILLEE DES SITES D'AMORCAGE ET DES CHEMINS DE PROPAGATION DES FISSURES A MONTRE L'INTERVENTION DE MECANISMES DIFFERENTS SELON LA TEMPERATURE. LE ROLE DETERMINANT DE L'ENVIRONNEMENT A DONNE LIEU A UNE ETUDE PLUS COMPLETE A 1000 C POUR PRECISER L'INTERACTION FATIGUE-OXYDATION