The growing use of polymer composites is leading to increasing demand for fractographic expertise. Fractography is the study of fracture surface morphologies and it gives an insight into damage and failure mechanisms, underpinning the development of physically-based failure criteria. In composites research it provides a crucial link between predictive models and experimental observations. Finally, it is vital for post-mortem analysis of failed or crashed polymer composite components, the findings of which can be used to optimise future designs.Failure analysis and fractography of polymer composites covers the following topics: methodology and tools for failure analysis; fibre-dominated failures; delamination-dominated failures; fatigue failures; the influence of fibre architecture on failure; types of defect and damage; case studies of failures due to overload and design deficiencies; case studies of failures due to material and manufacturing defects; and case studies of failures due to in-service factors.With its distinguished author, Failure analysis and fractography of polymer composites is a standard reference text for researchers working on damage and failure mechanisms in composites, engineers characterising manufacturing and in-service defects in composite structures, and investigators undertaking post-mortem failure analysis of components. The book is aimed at both academic and industrial users, specifically final year and postgraduate engineering and materials students researching composites and industry designers and engineers in aerospace, civil, marine, power and transport applications. - Examines the study of fracture surface morphologies in uderstanding composite structural behaviour - Discusses composites research and post-modern analysis of failed or crashed polymer composite components - Provides an overview of damage mechanisms, types of defect and failure criteria

The advantages of composite materials include a high specific strength and stiffness, formability, and a comparative resistance to fatigue cracking and corrosion. However, not forsaking these advantages, composite materials are prone to a wide range of defects and damage that can significantly reduce the residual strength and stiffness of a structure or result in unfavorable load paths. Emphasizing defect identification and restitution, Defects and Damage in Composite Materials and Structures explains how defects and damage in composite materials and structures impact composite component performance. Providing ready access to an extensive, descriptive list of defects and damage types, this must-have reference: Examines defect criticality in composite structures Recommends repair actions to restore structural integrity Discusses failure modes and mechanisms of composites due to defects Reviews NDI processes for finding and identifying defects in composite materials Relating defect detection methods to defect type, the author merges his experience in the field of in-service activities for composite airframe maintenance and repair with indispensable reports and articles on defects and damage in advanced composite materials from the last 50 years.

In contrast to metals, a composite material acquires an internal structure where the imprint of its manufacturing process history is a significant part of the internal structure’s makeup and in many cases determines how the material responds to external impulses. The performance for which a composite material is designed must therefore be assessed with due consideration to the manufacturing-induced features in the material volume. Failure theories based on homogenized composites cannot deliver reliable methodologies for performance assessment. This book details approaches that depart from traditional treatments by accounting for manufacturing defects in composite materials. It discusses how manufacturing defects are produced and how they affect the performance of composite materials. Serves as the only book to bring knowledge on manufacturing and failure modeling together in a coherent manner. Guides readers on mechanisms-based modeling with a focus on defects. Treats statistical simulation of microstructure with defects aimed at physical modeling. Covers manufacturing methods for polymer matrix composites. Describes failure modes in unidirectional composites and laminates in the presence of defects. Discusses fatigue damage in the presence of defects. This book is aimed at researchers in industry and academia in aerospace engineering, mechanical engineering, and materials science and engineering. It also serves as a reference for students taking advanced courses in composite materials.

Presents the latest strategies in the development and use of composite materials for large structures and the effects of defects Practical Design and Validation of Composites Structures: Effects of Defects offers an important guide to the use of fiber-reinforced composites and how they affect the durability and safety of engineering structures such as aircraft, ships, bridges, wind turbines as well as sporting equipment. The text draws on the authors’ direct experience in industry and academia to cover the most recent strategies in the development of composite structures and uniquely integrates the assessment of the effects of defects introduced during production. This comprehensive resource builds on an essential introduction to the characteristics of composites and the most common types of defects encountered in production. The authors review the recent manufacturing methods and technologies used for inspecting composite structures and the design issues related to an analysis of their failure and strength incorporating the variability of processing. The text also contains information on the latest regulatory requirements and the relevant standards associated with the testing and design within a robust design philosophy and approach. This important resource: Offers a comprehensive review of the most current regulatory developments in the use of composites for the construction of complex composite structures Presents information on the basic characteristics of composites Includes testing strategies for determining the impacts of production defects Reviews the most current manufacturing methods and inspection technologies in the field Contains methods for statistical analysis and processing of experimental effects of defects test data Written for professional engineers in mechanical engineering, automotive engineering, aerospace engineering, civil engineering, and energy engineering as well as industry and academic researchers, Practical Design and Validation of Composites Structures: Effects of Defects is the hands-on text that covers the essential information needed to understand the use of composites and how they affect complex engineering projects using composites.

Updated and improved, Stress Analysis of Fiber-Reinforced Composite Materials, Hyer's work remains the definitive introduction to the use of mechanics to understand stresses in composites caused by deformations, loading, and temperature changes. In contrast to a materials science approach, Hyer emphasizes the micromechanics of stress and deformation for composite material analysis. The book provides invaluable analytic tools for students and engineers seeking to understand composite properties and failure limits. A key feature is a series of analytic problems continuing throughout the text, starting from relatively simple problems, which are built up step-by-step with accompanying calculations. The problem series uses the same material properties, so the impact of the elastic and thermal expansion properties for a single-layer of FR material on the stress, strains, elastic properties, thermal expansion and failure stress of cross-ply and angle-ply symmetric and unsymmetric laminates can be evaluated. The book shows how thermally induced stresses and strains due to curing, add to or subtract from those due to applied loads.Another important element, and one unique to this book, is an emphasis on the difference between specifying the applied loads, i.e., force and moment results, often the case in practice, versus specifying strains and curvatures and determining the subsequent stresses and force and moment results. This represents a fundamental distinction in solid mechanics.

Bringing together materials mechanics and modelling, this book provides a complete guide to damage mechanics of composite materials for engineers.