ADHERENCE ET FROTTEMENT DES METAUX FONT INTERVENIR DES PHENOMENES PHYSICO-CHIMIQUES DEPENDANT DE LA TEMPERATURE. A HAUTE TEMPERATURE APPARAISSENT DES MECANISMES DIFFUSIONNELS QUI CONTRIBUENT A L'EXTENSION DES MICROJONCTIONS ENTRE LES ASPERITES. UNE ANALOGIE A ETE ETABLIE ENTRE L'ACCROISSEMENT DES COLLETS EN FRITTAGE ET PRESSAGE A CHAUD DE PARTICULES ET L'EVOLUTION DE CES JONCTIONS. ELLE A PERMIS DE TRACER DES DIAGRAMMES OU L'ON PEUT DELIMITER LES DOMAINES DE TEMPERATURE OU PREDOMINE L'ON OU L'AUTRE DE CES MECANISMES EN FONCTION DU RAYON DE COURBURE DES ASPERITES ET DE LA CHARGE. L'EXPERIMENTATION SOUS VIDE, DE 20 A 1100#OC A PERMIS DE FIXER LA TEMPERATURE CRITIQUE D'ADHERENCE ET DE FROTTEMENT EN FONCTION DE LA TEMPERATURE ONT ETE EXPLOITEES EN TENANT COMPTE DE LA COMPETITION ENTRE LA CROISSANCE DE L'AIRE DE CONTACT PAR FLUAGE OU FRITTAGE, ET LA CHUTE DES PROPRIETES MECANIQUES DU NICKEL. CES COURBES, TRACEES EN COORDONNEES D'ARRHENIUS, INDIQUENT L'INTERVENTION DE PROCESSUS THERMIQUEMENT ACTIVES QUI ONT ETE IDENTIFIES. DANS LE DOMAINE CONSIDERE, QUATRE MECANISMES DIFFUSIONNELS CONTRIBUENT AU TRANSPORT DE MATIERE: LA DIFFUSION SUPERFICIELLE A BASSE TEMPERATURE, FAIBLE CHARGE ET TEMPS DE CONTACT COURT, LA DIFFUSION INTERGRANULAIRE A TEMPERATURE INTERMEDIAIRE, LA DIFFUSION EN VOLUME POUR LES HAUTES TEMPERATURES

Recent research has led to a deeper understanding of the nature and consequences of interactions between materials on an atomic scale. The results have resonated throughout the field of tribology. For example, new applications require detailed understanding of the tribological process on macro- and microscales and new knowledge guides the rational

DES SUPERALLIAGES BASE NICKEL DEVELOPPES POUR DES CONDITIONS SEVERES DE TEMPERATURE ET DE CONTRAINTE, AINSI QUE LES PHASES INTERMETALLIQUES LES COMPOSANT, ONT ETE ETUDIES PAR FROTTEMENT INTERIEUR EN BALAYAGE DE FREQUENCE DE L'AMBIANTE A 1200 K. AUX BASSES TEMPERATURES (350-450 K), DES EFFETS DE RELAXATION LIES A LA PRESENCE D'INTERSTITIELS ONT ETE OBTENUS DANS DES MONOCRISTAUX NI#3AL+HF ET TIAL ET DANS LE SUPERALLIAGE MONOCRISTALLIN AM1. AUX HAUTES TEMPERATURES (>850 K), DANS TOUS LES MATERIAUX ETUDIES, UN PIC DE RELAXATION LIE A LA MONTEE DES DISLOCATIONS PAR AUTO-DIFFUSION A ETE OBSERVE. CE MECANISME INTERVIENT FORTEMENT SUR LES PROPRIETES MECANIQUES, PAR EXEMPLE DANS L'ALLIAGE DE REVETEMENT NICOCRALYTA, IL ENTRAINE L'APPARITION DE LA DUCTILITE DANS LE MATERIAU. DES EFFETS COMPLEXES D'AMORTISSEMENT LIE A L'ORDRE ONT ETE MIS EN EVIDENCE DANS PLUSIEURS CAS: PIC DE RELAXATION INTENSE DANS LES POLYCRISTAUX NI#3AL ORDONNE LIE A LA PRESENCE DE FAUTES D'ORDRE ET EFFET D'AMORTISSEMENT NON THERMIQUEMENT ACTIVE DANS LE SUPERALLIAGE AM1 ET UN POLYCRISTAL A GRAINS NI#3AL ORDONNE ET DESORDONNE. CES RESULTATS ORIGINAUX SONT ANALYSES EN TERME DE DESORDRE LOCAL ET DE GRADIENT CHIMIQUE

This title is designed to provide a clear and comprehensive overview of tribology. The book introduces the notion of a surface in tribology where a solid surface is described from topographical, structural, mechanical, and energetic perspectives. It also describes the principal techniques used to characterize and analyze surfaces. The title then discusses what may be called the fundamentals of tribology by introducing and describing the concepts of adhesion, friction, wear, and lubrication. The book focuses on the materials used in tribology, introducing the major classes of materials used, either in their bulk states or as coatings, including both protective layers and other coatings used for decorative purposes. Of especial importance to the tribology community are sections that provide the latest information on Nanotribology, Wear, Lubrication, and Wear-Corrosion: Tribocorrosion and Erosion-Corrosion.