PROBLEMES POSES PAR LE DEVELOPPEMENT DES MATERIAUX A MATRICE METALLIQUE RENFORCES PAR DES FIBRES COURTES. ETUDE REALISEE SUR L'ALLIAGE DE FONDERIE AS7G03, A BASE AL, CONTENANT 6,5 A 7,5 % DE SI, 0,25 A 0,4 % DE MG, 0,1 A 0,2 % DE TI, ET LA FICHE DE CARBURE DE SILICIUM NICALEN. FABRICATION DU MATERIAU COMPOSITE PAR RHEOMOULAGE AVEC BRASSAGE MECANIQUE EN COURS DE SOLIDIFICATION. INTERPRETATION DES PROPRIETES MECANIQUES DU COMPOSITE EN CONSIDERANT A LA FOIS L'INFLUENCE DE LA FRACTION VOLUMIQUE DE FIBRES ET L'AUGMENTATION DE RESISTANCE DE LA MATRICE LIEE A CETTE ADDITION. ETUDE COMPARATIVE DES COMPOSITES ELABORES A L'ETAT SEMI-SOLIDE OU PAR INFILTRATION

CE TRAVAIL CONCERNE L'ELABORATION PAR ELECTROFORMAGE DE SPHERES CREUSES A HAUTES CARACTERISTIQUES THERMOMECANIQUES DESTINEES A LA REALISATION D'UN NOUVEAU MATERIAU COMPOSITE OBTENU PAR BRASAGE DES SPHERES SUIVANT UNE STRUCTURE ORDONNEE. NOTRE CHOIX S'EST PORTE SUR LA SYNTHESE PAR CODEPOSITION ELECTROCHIMIQUE DE MATERIAUX COMPOSITES A MATRICE METALLIQUE (M.M.C.) A BASE DE NICKEL RENFORCE PAR DE L'ALUMINE OU DU SESQUIOXYDE DE CHROME. DANS UNE PREMIERE PARTIE DE NOS TRAVAUX, NOUS SYNTHETISONS DES POUDRES SUBMICRONIQUES DE CES DEUX OXYDES DISPERSABLES EN SOLUTION AQUEUSE. NOUS PRESENTONS ENSUITE UNE ETUDE SYSTEMATIQUE DE L'INFLUENCE DES PARAMETRES ELECTROCHIMIQUES SUR LA CODEPOSITION EN COURANT CONTINU. AFIN D'ACCROITRE LA PROPORTION DE PARTICULES CODEPOSEES NOUS AVONS UTILISE UN PLAN D'EXPERIENCES SIMPLEX APPLIQUE A LA CODEPOSITION PAR COURANTS PULSES. LA FRACTION VOLUMIQUE D'ALUMINE CODEPOSE A PU ETRE ACCRUE DE 45% PAR RAPPORT AU COURANT CONTINU. UNE AUTRE TECHNIQUE A CONSISTE A DOPER EN SURFACE L'ALUMINE PAR DU SESQUIOXYDE CR#2O#3 ET PAR DE L'OXYDE DE NICKEL NIO. LA PROGRESSION EST SIGNIFICATIVE; LA FRACTION VOLUMIQUE CODEPOSEE EVOLUE DE 2,4 A 3 ET 3,4%. LES COMPOSITES SONT ENSUITE CARACTERISES D'UN POINT DE VUE MICROSTRUCTURAL ET THERMOMECANIQUE. CES MATERIAUX PRESENTENT AVANT ET APRES TRAITEMENT THERMIQUE DES PROPRIETES TRES SUPERIEURES AU NICKEL PUR. NOUS MONTRONS QUE LE MODE DE RENFORCEMENT EST IMPUTABLE A DES EFFETS COMPLEXES ET CONJUGUES DE PLUSIEURS PROCESSUS ELEMENTAIRES

L'EFFICACITE DES TURBINES PEUT ETRE AMELIOREE EN REDUISANT LE POIDS DE LEURS PIECES TOURNANTES. GRACE A LEUR BONNE TENUE EN TEMPERATURE ET A LEURS BONNES PROPRIETES DANS LE SENS DES FIBRES, LES COMPOSITES SIC/TI SONT DES CANDIDATS SERIEUX POUR LA FABRICATION D'ANNEAUX AUBAGES MONOBLOCS AVEC UNE REDUCTION DE POIDS DE 50%. CEPENDANT, UN FORT ETAT DE CONTRAINTES TRIAXIAL EST GENERE DANS LE DISQUE EN ROTATION. UNE MEILLEURE COMPREHENSION DES PROPRIETES TRANSVERSE, SOUVENT FAIBLES POUR DE TELS COMPOSITES, EST DONC NECESSAIRE. LA DEMARCHE DE CE TRAVAIL PEUT SE DECOMPOSER EN DEUX PARTIES : 1/ DU MACRO AU MICRO : POUR UNE MEILLEURE COMPREHENSION DES PHENOMENES. DANS CETTE PARTIE, ON DETERMINE QUELS SONT LES MECANISMES DES DEFORMATIONS ET D'ENDOMMAGEMENT MIS EN JEU LORS D'UN ESSAI DE FLUAGE TRAVERS, FINALEMENT L'ECHELLE MICRO PERTINENTE SERA DETERMINEE. CE TRAVAIL REPOSE SUR DES ASPECTS EXPERIMENTAUX (ESSAIS DE FLUAGE, OBSERVATIONS MICROGRAPHIQUES, ETC.), SUR DES ASPECTS NUMERIQUES (MODELISATION PAR ELEMENTS FINIS, IDENTIFICATION DE LOIS DE COMPORTEMENTS, ETC.), ET SUR DES ASPECTS PLUS MATERIAUX (TEXTURE LOCALE DE LA MATRICE, MECANISMES DE DEFORMATION PAR GLISSEMENT, ETC.). LES RESULTATS OBTENUS REVELENT L'IMPORTANCE DU COMPORTEMENT INTERFACIAL ET DE LA TEXTURE LOCALE SUR LE COMPORTEMENT MACROSCOPIQUE DU COMPOSITE. 2/ DU MICRO AU MACRO : VERS LE CALCUL DE STRUCTURE. LE BUT DE CETTE PARTIE EST DE DEVELOPPER UNE LOI DE COMPORTEMENT MACROSCOPIQUE PRENANT EN COMPTE LES ECHELLES MICRO PERTINENTES PRECEDEMMENT DETERMINEES. CES DEVELOPPEMENTS SONT BASES SUR LES TRAVAUX DE DVORAK, ET LA LOI DE COMPORTEMENT MACROSCOPIQUE EST ECRITE DE L'ECHELLE MICRO (ECHELLE DU GRAIN ET ECHELLE DE L'INTERFACE) JUSQU'A L'ECHELLE MACRO. LA DERNIERE ETAPE CONSISTE A REALISER LE CALCUL COMPLET DU DISQUE.

This unique and practical book provides quick and easy access to data on the physical and chemical properties of all classes of materials. The second edition has been much expanded to include whole new families of materials while many of the existing families are broadened and refined with new material and up-to-date information. Particular emphasis is placed on the properties of common industrial materials in each class. Detailed appendices provide additional information, and careful indexing and a tabular format make the data quickly accessible. This book is an essential tool for any practitioner or academic working in materials or in engineering.