ETUDE DU COMPORTEMENT, PAR VOLTAMMETRIE CYCLIQUE ET CHRONOPOTENTIOMETRIE, DANS NA::(2)O-4B::(2)O::(3), NA::(2)O-2B::(2)O::(3) ET 3NA::(2)O-B::(2)O::(3), ENTRE 750 ET 1000 C, DE CES TROIS METAUX.

ETUDE DU COMPORTEMENT, PAR VOLTAMMETRIE CYCLIQUE ET CHRONOPOTENTIOMETRIE, DANS NA::(2)O-4B::(2)O::(3), NA::(2)O-2B::(2)O::(3) ET 3NA::(2)O-B::(2)O::(3), ENTRE 750 ET 1000 C, DE CES TROIS METAUX

ETUDE DE LA CORROSION EN MILIEU DE SELS FONDUS (MELANGES NA::(2)SO::(4), NA::(2)CO::(3), NACL ET NA::(2)CO::(3), NA::(2)S, NA::(2)SO::(4), NACL) POUR DES TEMPERATURES COMPRISES ENTRE 300**(O)C ET 900**(O)C D'ALLIAGES DE NICKEL (IN800, IN600...) ET D'ACIERS INOXYDABLES (Z6CN1810, Z12CN25-20...). MESURE DES VARIATIONS DE MASSE ET EXAMEN DES PRODUITS FORMES. INFLUENCE D'UN TRAITEMENT DE SURFACE. INFLUENCE DE LA COMPOSITION DE L'ALLIAGE. MECANISME DE CORROSION

MISE EN EVIDENCE DE LA FORMATION DES COMPOSES DEFINIS TINI::(3), TINI ET TI::(2)NI SUR LE NICKEL DES 600**(O)C ET DE FE::(2)TI ET FETI SUR LE FER AU-DELA DE 800**(O)C PRECEDANT LA FORMATION DE TITANE PUR