LE COMPORTEMENT ELECTROCHIMIQUE A LA CORROSION DE L'ACIER AU CARBONE API K55 DANS LE FLUIDE GEOTHERMAL A ETE ETUDIE EN PRESENCE ET EN L'ABSENCE DE DIFFERENTS INHIBITEURS A BASE D'AMINES, POTENTIELLEMENT ADAPTES AUX PROBLEMES DE CORROSION-DEPOT DANS LES INSTALLATIONS GEOTHERMIQUES EXPLOITANT L'AQUIFERE DU DOGGER DU BASSIN PARISIEN. LA CONJUGAISON DES TRAVAUX EFFECTUES AU LABORATOIRE ET SUR SITES, SOUS DIFFERENTES CONDITIONS PHYSICO-CHIMIQUES ET D'EXPLOITATION, NOUS ONT PERMIS DE COMPRENDRE L'ACTION DES DIFFERENTS PARAMETRES RECONNUS COMME DETERMINANTS DANS LES PROCESSUS DE CORROSION TELS QUE, LA CONCENTRATION EN SULFURE D'HYDROGENE ET EN IONS CHLORURES, LE DEBIT D'EXPLOITATION ET LES DEPOTS DE SULFURES DE FER. LE SULFURE D'HYDROGENE ACTIVE LES REACTIONS ANODIQUES ET CATHODIQUES DANS LE DOMAINE DE CONCENTRATION EXPLORE (0-100 MG/L), L'AUGMENTATION DE SA CONCENTRATION REDUIT L'EFFICACITE DES INHIBITEURS ORGANIQUES DE CORROSION. LES IONS CHLORURES AUGMENTENT L'AGRESSIVITE DU FLUIDE DANS LES MILIEUX FAIBLEMENT AGITES ET REDUISENT L'EFFICACITE DES INHIBITEURS A BASE D'AMMONIUM QUATERNAIRES. L'AUGMENTATION DU DEBIT REDUIT LA VITESSE DE CORROSION AINSI QUE L'EPAISSEUR DES DEPOTS DE CORROSION. LES DEPOTS DE CORROSION SONT MAJORITAIREMENT CONSTITUES DE SULFURES DE FER ET SE PRESENTENT SOUS FORME DE DEUX COUCHES DISTINCTES: LA PREMIERE, MINCE, DU COTE METAL EST FORMEE D'HYDROXYDES ET D'HYDROXYCHLORURES DE FER ET LA SECONDE EXTERNE PLUS EPAISSE ET CONSTITUEE MAJORITAIREMENT DE SULFURES DE FER. CES DEPOTS, POREUX ET PLUS NOBLES QUE LE FER, NE SONT PAS PROTECTEURS ET PEUVENT PARTICIPER A L'ACTIVATION DE LA CORROSION PAR TRANSFERT DES SITES CATHODIQUES SUR LEUR SURFACE. LA CINETIQUE DE CORROSION DE L'ACIER AU CARBONE DANS CE MILIEU EST SOUS CONTROLE MIXTE, TRANSFERT DIFFUSION. LES INHIBITEURS DE CORROSION TESTES PRESENTENT UNE EFFICACITE SATISFAISANTE. L'AMINE GRASSE EST L'INHIBITEUR LE PLUS ADAPTE, PUISQUE SON EFFICACITE N'EST ALTEREE NI PAR LA PRESENCE DES DEPOTS, NI PAR UN MILIEU STAGNANT OU AGITE, SA FORTE VITESSE D'ADSORPTION AINSI QUE SON FAIBLE CARACTERE ANODIQUE DIMINUENT LE RISQUE DE CORROSION PAR PIQURES. POUR L'INVESTIGATION DE FORMULATIONS INHIBITRICES, DEUX SERIES DE TESTS ELECTROCHIMIQUES SONT PROPOSEES. ELLES PERMETTENT DE DEFINIR LES CONDITIONS OPTIMALES DE L'UTILISATION DE L'ACIER AU CARBONE (ET DE TOUT AUTRE MATERIAU METALLIQUE) DANS UN MILIEU CORROSIF DONNE ET LE CHOIX DE L'INHIBITEUR ADAPTE

LA PRESENTE ETUDE TENTE D'APPORTER QUELQUES ELEMENTS NOUVEAUX A LA CONNAISSANCE DE LA FISSURATION SOUS CONTRAINTE DU FER ET DES ACIERS DOUX ASSISTEE PAR UN ENVIRONNEMENT RICHE EN IONS HYDROGENOCARBONATE, PHENOMENE AUJOURD'HUI UNANIMEMENT RECONNU COMME CAUSE DE NOMBREUX CAS DE RUPTURE DE CANALISATIONS DE TRANSPORT D'HYDROCARBURES OU DE GAZ SOUMISES A UNE PROTECTION CATHODIQUE. L'ETUDE DES PHENOMENES ELECTROCHIMIQUES REGISSANT LA DISSOLUTION DU FER DANS LE DOMAINE DE POTENTIEL CORRESPONDANT A LA TRANSITION ACTIVITE-PASSIVITE (ZONE SENSIBLE VIS-A-VIS DE LA CORROSION SOUS CONTRAINTE), LA CARACTERISATION EX-SITU DES DEPOTS DE SURFACE (NOTAMMENT L'ANALYSE COMPOSITIONNELLE QUALITATIVE ET QUANTITATIVE PAR SPECTROSCOPIE INFRAROUGE, LA MESURE DE LA CONDUCTION ELECTRIQUE A L'INTERIEUR DES COUCHES) PERMETTENT D'ETABLIR UNE CORRELATION ENTRE LA NATURE ET L'ABONDANCE DES DIVERS PRODUITS DE CORROSION D'UNE PART ET LA SUSCEPTIBILITE DU SYSTEME AU RISQUE D'ENDOMMAGEMENT CONSIDERE ICI D'AUTRE PART. LES HYDROXYCARBONATES MIXTES DE FER II ET FER III A 25 ET 50C, LE CARBONATE DE FER FECO#3 A 80C, SE REVELENT ETRE LES CONSTITUANTS MAJORITAIRES DES SURFACES DANS LES CONDITIONS OU LE METAL FISSURE. UNE CRITIQUE D'UN MODELE PROPOSE DANS LA LITTERATURE, SELON LEQUEL LA SUSCEPTIBILITE A LA CORROSION SOUS CONTRAINTE DU SYSTEME EST CORRELEE A LA CONSTANTE DE TEMPS DE LA BOUCLE BF DE L'ADMITTANCE ELECTROCHIMIQUE, EST SUGGEREE. L'ETUDE DE LA FISSURATION SOUS CONTRAINTE MECANIQUE, ENTREPRISE DANS LE CADRE D'ESSAIS DE TRACTION A VITESSE LENTE SUR EPROUVETTES LISSES MAINTENUES A POTENTIEL CONTROLE, NOUS PERMET DE PROPOSER UNE MODELISATION DES PHENOMENES ELECTROCHIMIQUES MIS EN JEU AU COURS DE L'ESSAI MECANIQUE, VERIFIEE PAR LE BIAIS D'ARRETS INTERMITTENTS DE LA TRACTION. L'EFFET DE L'ETAT DE CONTRAINTES INITIAL EST EGALEMENT PRIS EN COMPTE. LES MESURES D'IMPEDANCE ELECTROCHIMIQUE REALISEES EN COURS D'ESSAI DE TRACTION NE PERMETTENT APPAREMMENT PAS DE METTRE EN EVIDENCE D'EVOLUTION SIGNIFICATIVE DU DIAGRAMME EN FONCTION DU NIVEAU D'AVANCEMENT DE LA FISSURATION

ETUDE THEORIQUE DES PHENOMENES DE CORROSION ELECTROCHIMIQUE DES ACIERS INOXYDABLES AUSTENITIQUES EN MILIEU ACIDE. INFLUENCE DES ELEMENTS D'ALLIAGE SUR LA RESISTANCE A LA CORROSION DE L'ACIER (MO) OU A L'ACCELERATION DU PHENOMENE (S ET SI)

CORROSION PAR PIQURES DU FER DANS FECL::(2). AMORCAGE ET CROISSANCE DES PIQURES