Fracture Toughness Testing of Zircaloy-2 Pressure Tube Material with Radial Hydrides Using Direct-Current Potential Drop
Title | Fracture Toughness Testing of Zircaloy-2 Pressure Tube Material with Radial Hydrides Using Direct-Current Potential Drop PDF eBook |
Author | PH. Davies |
Publisher | |
Pages | 22 |
Release | 1986 |
Genre | Compact tension specimen |
ISBN |
This paper addresses problems involved in measuring fracture toughness of thin pressure tube material which, in the presence of radial-axial hydrides, undergoes a significant brittle to ductile fracture transition. Compact tension specimens (~5 mm thickness) are machined from flattened tensile strips of Zircaloy-2 in which radial hydrides (30 to 100 ppm hydrogen) are produced by precipitation under stress. Axial fracture toughness is determined for the unirradiated material between room temperature and 300°C using the dc potential drop method. At low and intermediate temperatures crack growth is governed predominantly by the presence of the radial hydrides, and the potential drop is shown to underestimate crack extension due to short-circuiting across tight crack faces. In the upper shelf regime where crack extension is governed mainly by the flow properties of the matrix, the potential drop overestimates crack extension due to through-thickness yielding. It is shown that good, reproducible results can be obtained by careful data analysis using individual specimen calibrations.
Fracture Mechanics
Title | Fracture Mechanics PDF eBook |
Author | John H. Underwood |
Publisher | ASTM International |
Pages | 837 |
Release | 1986 |
Genre | Fractura de sólidos |
ISBN | 0803104723 |
Zirconium in the Nuclear Industry
Title | Zirconium in the Nuclear Industry PDF eBook |
Author | Leo F. P. Van Swam |
Publisher | ASTM International |
Pages | 781 |
Release | 1989 |
Genre | Nuclear fuel claddings |
ISBN | 0803111991 |
Zirconium in the Nuclear Industry: Tenth International Symposium
Title | Zirconium in the Nuclear Industry: Tenth International Symposium PDF eBook |
Author | A. M. Garde |
Publisher | ASTM International |
Pages | 805 |
Release | 1994 |
Genre | Nuclear fuel claddings |
ISBN | 0803120117 |
Comprehensive Structural Integrity
Title | Comprehensive Structural Integrity PDF eBook |
Author | Ian Milne |
Publisher | Elsevier |
Pages | 4647 |
Release | 2003-07-25 |
Genre | Business & Economics |
ISBN | 0080490735 |
The aim of this major reference work is to provide a first point of entry to the literature for the researchers in any field relating to structural integrity in the form of a definitive research/reference tool which links the various sub-disciplines that comprise the whole of structural integrity. Special emphasis will be given to the interaction between mechanics and materials and structural integrity applications. Because of the interdisciplinary and applied nature of the work, it will be of interest to mechanical engineers and materials scientists from both academic and industrial backgrounds including bioengineering, interface engineering and nanotechnology. The scope of this work encompasses, but is not restricted to: fracture mechanics, fatigue, creep, materials, dynamics, environmental degradation, numerical methods, failure mechanisms and damage mechanics, interfacial fracture and nano-technology, structural analysis, surface behaviour and heart valves. The structures under consideration include: pressure vessels and piping, off-shore structures, gas installations and pipelines, chemical plants, aircraft, railways, bridges, plates and shells, electronic circuits, interfaces, nanotechnology, artificial organs, biomaterial prostheses, cast structures, mining... and more. Case studies will form an integral part of the work.
Fracture Toughness Evaluation for Zircaloy-2 Pressure Tubes with the Electric-Potential Method
Title | Fracture Toughness Evaluation for Zircaloy-2 Pressure Tubes with the Electric-Potential Method PDF eBook |
Author | FH. Huang |
Publisher | |
Pages | 17 |
Release | 1993 |
Genre | Annealing of metals |
ISBN |
Zircaloy is commonly used for the cladding or pressure tubes in commercial nuclear reactors because of its strength, corrosion resistance, and low absorption of thermal neutrons. Fracture toughness test techniques using small samples fabricated from archival materials from the N Reactor pressure tubes of Zircaloy-2 were developed to study the factors affecting tube fracture toughness. Compact tension specimen thickness was limited by the wall thickness (7 mm) of the tubes. Specimens (5 mm thick) were prepared for fracture toughness testing, and results were analyzed using the J-integral approach. To reduce the high cost of irradiated specimen testing and to more easily precrack specimens remotely, single-specimen potential drop techniques were employed to evaluate the fracture toughness of Zircaloy-2.
Fracture Mechanics
Title | Fracture Mechanics PDF eBook |
Author | |
Publisher | |
Pages | 856 |
Release | 1986 |
Genre | Fracture mechanics |
ISBN |