ETUDE DU COMPORTEMENT DE TI DANS HCL CONCENTRE, DESELERE OU NON. DIAGRAMMES DE POLARISATION ET MESURES D'IMPEDANCE

CE TRAVAIL A POUR OBJET L'ETUDE DU COMPORTEMENT ELECTROCHIMIQUE DE MATERIAUX INDUSTRIELS CONFRONTES A UN ENVIRONNEMENT AQUEUX A TEMPERATURE ET PRESSION ELEVEES. IL TRAITE NOTAMMENT DU NICKEL, DE SES ALLIAGES UTILISES DANS LES GENERATEURS DE VAPEUR ET DU TITANE, EMPLOYE, PAR EXEMPLE, DANS LES EVAPORATEURS. L'UTILISATION DES METHODES ELECTROCHIMIQUES DANS CES CONDITIONS PARTICULIERES A CONDUIT A LA REALISATION DE DEUX DISPOSITIFS SPECIFIQUES CAPABLES, PAR LES SOLUTIONS TECHNIQUES ADOPTEES (INERTIE CHIMIQUE DES AUTOCLAVES, EXPLOITATION D'UNE REFERENCE INTERNE: ELECTRODE DYNAMIQUE A HYDROGENE, ELECTRODE TOURNANTE, MAITRISE DE LA PHASE, ...), D'ASSURER, JUSQU'A 300C ET 150 BAR, UNE INFORMATION AUSSI SURE ET COMPLETE QUE CELLE OBTENUE DANS DES CONDITIONS HABITUELLES DE TEMPERATURE ET DE PRESSION. AINSI, L'ACCES AUX COURANTS STATIONNAIRES ET A L'IMPEDANCE ELECTROCHIMIQUE PERMET D'AVANCER LES ELEMENTS D'UNE MODELISATION DE LA DISSOLUTION ET DE LA PASSIVATION DU TITANE EN MILIEU CHLORURE, DANS LAQUELLE LA FORMATION DE L'OXYDE TIO2 TIENT UNE PLACE IMPORTANTE. SUR LA BASE DE CE RESULTAT, UN MECANISME PROPOSE POUR LE NICKEL ACTIVE EN MILIEU BASIQUE FAIBLEMENT IONISE AVEC UNE INCIDENCE PARTICULIERE DE L'OXYDE NIO EST APPLIQUE A CERTAINS ALLIAGES, NOTAMMENT L'ALLIAGE 800. LE ROLE PREDOMINANT DU NICKEL SUR LA DISSOLUTION DE CES ALLIAGES PERMET DE SITUER LES RISQUES D'UNE EXPLOITATION EN EAU CHAUDE PRESSURISEE