It is estimated that about 40% of the annual production of metals is used to repair or replace materials damaged by corrosion. Corrosion causes waste of the natural material and energy resources, it creates serious materials problems for many technologies and adversely affects almost every area of engineering. The use of metals in various aggressive environments has resulted in an extremely wide diversity of corrosion problems. This book presents a collection of concise reviews written by experts in the field on selected topics of metallic corrosion and on some aspects of interaction of hydrogen with metals. A comprehensive range of problems is examined including localized corrosion, high temperature corrosion in liquid metals and molten salts, transport control in corrosion processes, entry of hydrogen into metals, hydrogen embrittlement, and hydrogen reactions with metals. The variety of topics covered in the book will provide corrosion scientists, engineers, university lecturers and students alike with an interdisciplinary approach to solving problems of materials degradation and surface processes in metal corrosion.

Hydrogen in Steel: Effect of Hydrogen on Iron and Steel During Production, Fabrication, and Use focuses on the effect of hydrogen on iron and steel during production, fabrication, and use. Topics covered range from the solubility of hydrogen in iron and ferrous alloys to the diffusion and permeation of hydrogen through iron and steel. Electrochemical problems related to the ability of iron to absorb hydrogen from aqueous solutions are also considered. Comprised of 19 chapters, this book begins with a detailed treatment of the nature and properties of metal-hydrogen systems, paying particular attention to the behavior of hydrogen in the bulk of the metal phase and the mechanism of reactions between metals and hydrogen or hydrogen-producing compounds. The reader is then introduced to the solubility of hydrogen in iron and ferrous alloys as well as the nature of the final product of the hydrogen-iron interaction. Subsequent chapters deal with dimensional changes and stresses produced in steel by cathodically evolved hydrogen; the effects of hydrogen on the physical, mechanical, and chemical properties of iron and steel; influence of welding on hydrogen; and sulfide corrosion cracking of steel. The effects of pickling on steel are also examined, along with the blistering and embrittlement caused by hydrogen on the base metal during electroplating. This book will be of value to students and practitioners in the field of physical chemistry.

Corrosion engineers today spend enormous amounts of time and money searching multiple detailed sources and variable industry-specific standards to locate known remedies to corrosion equipment problems. Corrosion Atlas Series is the first centralized collection of case studies containing challenges paired directly with solutions together in one location. The second release of content in the series, Corrosion Atlas Case Studies: 2021 Edition, gives engineers expedient daily corrosion solutions for common industrial equipment, no matter the industry. Providing a purely operational level view, this reference is designed as concise case studies categorized by material and includes content surrounding the phenomenon, equipment appearance supported by a color image, time of service, conditions where the corrosion occurred, cause, and suggested remedies within each case study. Additional reference listings for deeper understanding beyond the practical elements are also included. Rounding out with an introductory foundational layer of corrosion principles critical to all engineers, Corrosion Atlas Case Studies: 2021 Edition delivers the daily tool required for engineers today to solve their equipment's corrosion problems. - Solves equipment failure with easy-to-find remedies organized by essential elements such as materials, system, part, cause, environmental, and phenomenon - Grasps fundamental corrosion elements on all major industrial pieces of equipment, no matter the industry - Identify failures by appearance with color figures within each case study

This book deals with basic principles such as chemical equilibrium as well as chemical processes. These concepts make up the basic tools necessary to design a more efficient system to solve environmental problems. This book can be used as a textbook for a university-level course. It can also serve as an excellent source for professional research in the field of environmental engineering or environmental science.

Textbook; grad.

The problem of stress corrosion cracking (SCC), which causes sudden failure of metals and other materials subjected to stress in corrosive environment(s), has a significant impact on a number of sectors including the oil and gas industries and nuclear power production. Stress corrosion cracking reviews the fundamentals of the phenomenon as well as examining stress corrosion behaviour in specific materials and particular industries.The book is divided into four parts. Part one covers the mechanisms of SCC and hydrogen embrittlement, while the focus of part two is on methods of testing for SCC in metals. Chapters in part three each review the phenomenon with reference to a specific material, with a variety of metals, alloys and composites discussed, including steels, titanium alloys and polymer composites. In part four, the effect of SCC in various industries is examined, with chapters covering subjects such as aerospace engineering, nuclear reactors, utilities and pipelines.With its distinguished editors and international team of contributors, Stress corrosion cracking is an essential reference for engineers and designers working with metals, alloys and polymers, and will be an invaluable tool for any industries in which metallic components are exposed to tension, corrosive environments at ambient and high temperatures. - Examines the mechanisms of stress corrosion cracking (SCC) presenting recognising testing methods and materials resistant to SCC - Assesses the effect of SCC on particular metals featuring steel, stainless steel, nickel-based alloys, magnesium alloys, copper-based alloys and welds in steels - Reviews the monitoring and management of SCC and the affect of SCC in different industries such as petrochemical and aerospace