LE COMPORTEMENT ELECTROCHIMIQUE A LA CORROSION DE L'ACIER AU CARBONE API K55 DANS LE FLUIDE GEOTHERMAL A ETE ETUDIE EN PRESENCE ET EN L'ABSENCE DE DIFFERENTS INHIBITEURS A BASE D'AMINES, POTENTIELLEMENT ADAPTES AUX PROBLEMES DE CORROSION-DEPOT DANS LES INSTALLATIONS GEOTHERMIQUES EXPLOITANT L'AQUIFERE DU DOGGER DU BASSIN PARISIEN. LA CONJUGAISON DES TRAVAUX EFFECTUES AU LABORATOIRE ET SUR SITES, SOUS DIFFERENTES CONDITIONS PHYSICO-CHIMIQUES ET D'EXPLOITATION, NOUS ONT PERMIS DE COMPRENDRE L'ACTION DES DIFFERENTS PARAMETRES RECONNUS COMME DETERMINANTS DANS LES PROCESSUS DE CORROSION TELS QUE, LA CONCENTRATION EN SULFURE D'HYDROGENE ET EN IONS CHLORURES, LE DEBIT D'EXPLOITATION ET LES DEPOTS DE SULFURES DE FER. LE SULFURE D'HYDROGENE ACTIVE LES REACTIONS ANODIQUES ET CATHODIQUES DANS LE DOMAINE DE CONCENTRATION EXPLORE (0-100 MG/L), L'AUGMENTATION DE SA CONCENTRATION REDUIT L'EFFICACITE DES INHIBITEURS ORGANIQUES DE CORROSION. LES IONS CHLORURES AUGMENTENT L'AGRESSIVITE DU FLUIDE DANS LES MILIEUX FAIBLEMENT AGITES ET REDUISENT L'EFFICACITE DES INHIBITEURS A BASE D'AMMONIUM QUATERNAIRES. L'AUGMENTATION DU DEBIT REDUIT LA VITESSE DE CORROSION AINSI QUE L'EPAISSEUR DES DEPOTS DE CORROSION. LES DEPOTS DE CORROSION SONT MAJORITAIREMENT CONSTITUES DE SULFURES DE FER ET SE PRESENTENT SOUS FORME DE DEUX COUCHES DISTINCTES: LA PREMIERE, MINCE, DU COTE METAL EST FORMEE D'HYDROXYDES ET D'HYDROXYCHLORURES DE FER ET LA SECONDE EXTERNE PLUS EPAISSE ET CONSTITUEE MAJORITAIREMENT DE SULFURES DE FER. CES DEPOTS, POREUX ET PLUS NOBLES QUE LE FER, NE SONT PAS PROTECTEURS ET PEUVENT PARTICIPER A L'ACTIVATION DE LA CORROSION PAR TRANSFERT DES SITES CATHODIQUES SUR LEUR SURFACE. LA CINETIQUE DE CORROSION DE L'ACIER AU CARBONE DANS CE MILIEU EST SOUS CONTROLE MIXTE, TRANSFERT DIFFUSION. LES INHIBITEURS DE CORROSION TESTES PRESENTENT UNE EFFICACITE SATISFAISANTE. L'AMINE GRASSE EST L'INHIBITEUR LE PLUS ADAPTE, PUISQUE SON EFFICACITE N'EST ALTEREE NI PAR LA PRESENCE DES DEPOTS, NI PAR UN MILIEU STAGNANT OU AGITE, SA FORTE VITESSE D'ADSORPTION AINSI QUE SON FAIBLE CARACTERE ANODIQUE DIMINUENT LE RISQUE DE CORROSION PAR PIQURES. POUR L'INVESTIGATION DE FORMULATIONS INHIBITRICES, DEUX SERIES DE TESTS ELECTROCHIMIQUES SONT PROPOSEES. ELLES PERMETTENT DE DEFINIR LES CONDITIONS OPTIMALES DE L'UTILISATION DE L'ACIER AU CARBONE (ET DE TOUT AUTRE MATERIAU METALLIQUE) DANS UN MILIEU CORROSIF DONNE ET LE CHOIX DE L'INHIBITEUR ADAPTE

DENOMBREMENT DES BACTERIES SULFATOREDUCTRICES DANS LES DEPOTS DE CORROSION SUR LA COLONNE DE PRODUCTION D'UN PUITS GEOTHERMIQUE. ISOLEMENT ET CARACTERISATION DE DEUX ESPECES NOUVELLES, THERMOPILES, DE DESULFOTOMACULUM. UTILISATION DE TECHNIQUES ELECTROCHIMIQUES DE MESURE DE LA CORROSION POUR EN ETUDIER LES MECANISMES. SUIVI DES VARIATIONS DU POTENTIEL DE CORROSION DU METAL (ACIER AU CARBONE), CALCUL DES VITESSES DE CORROSION PAR DOSAGE DU FER ET PAR EXTRAPOLATION DES DROITES DE TAFEL, ESTIMATION DE LA BIOMASSE BACTERIENNE SUR LES SURFACES METALLIQUES (DOSAGE DES PHOSPHOLIPIDES), CONSTITUTION D'UNE PILE BIOLOGIQUE, ETUDE DE LA COMPOSITION CHIMIQUE DES COUCHES FORMEES SUR LES SURFACES

CE TRAVAIL A ETE CONSACRE A L'ETUDE DE L'INHIBITION DE LA CORROSION D'UN ACIER AU CARBONE DANS UNE SOLUTION AEREE DE CHLORURE DE SODIUM PAR L'ASSOCIATION DU CHLORURE DE ZINC ET D'UN ACIDE PHOSPHONIQUE. L'ETUDE A ETE REALISEE A L'AIDE DE MESURES ELECTROCHIMIQUES ASSOCIEES A DES ANALYSES DE SURFACE POUR DETERMINER LE MECANISME D'ACTION ET OBTENIR UNE MEILLEURE CONNAISSANCE DU FILM FORME SUR LA SURFACE DE L'ACIER. LA COMPARAISON DE L'ACTION INHIBITRICE DU CHLORURE DE ZINC, DE L'ACIDE PHOSPHONIQUE ET D'UN MELANGE CONTENANT CES DEUX COMPOSES A REVELE UNE AMELIORATION TRES IMPORTANTE DE LA PROTECTION DANS LE CAS DU MELANGE ET CE, POUR UNE VALEUR PLUS FAIBLE DES CONCENTRATIONS DES COMPOSES DANS LE MELANGE PAR RAPPORT A LA CONCENTRATION DES COMPOSES TESTES SEPAREMENT. LES RESULTATS OBTENUS A TRAVERS LES ETUDES REALISEES POUR DIFFERENTES VALEURS DU PH, ONT MONTRE QUE L'ACTION ANODIQUE DU MELANGE EST APPORTEE PAR L'ACIDE PHOSPHONIQUE QUI EST CAPABLE DE COMPLEXER LES IONS DIVALENTS. L'ACTION CATHODIQUE EST LIEE A LA PRESENCE DU CHLORURE DE ZINC QUI CONDUIT A LA PRECIPITATION DE L'HYDROXYDE DE ZINC SUR LES ZONES CATHODIQUES. LES DIAGRAMMES D'IMPEDANCE ELECTROCHIMIQUE ET LES COURBES DE POLARISATION OBTENUS POUR LE MELANGE INHIBITEUR ONT MONTRE QUE LES REACTIONS QUI SE PRODUISENT A L'INTERFACE NE SONT PAS CONTROLEES PAR LE TRANSPORT DE MATIERE. LE FILM INHIBITEUR EST RELATIVEMENT COMPACT, FIN ET IMPERMEABLE A LA DIFFUSION IONIQUE OU MOLECULAIRE. LA CORROSION SE PRODUIT SUR LES DEFAUTS DU FILM OU DE LA SURFACE DE L'ACIER. L'ANALYSE DU FILM FORME A LA SURFACE DE L'ACIER PAR XPS A MONTRE QU'IL ETAIT HOMOGENE EN COMPOSITION ET FORME DE ZN, P, CL ET O. LE SPECTRE INFRAROUGE EN INCIDENCE RASANTE A REVELE LA REACTION DE L'ACIDE PHOSPHONIQUE AVEC L'HYDROXYDE DE ZINC POUR FORMER UN SEL METALLIQUE