The advantages of composite materials include a high specific strength and stiffness, formability, and a comparative resistance to fatigue cracking and corrosion. However, not forsaking these advantages, composite materials are prone to a wide range of defects and damage that can significantly reduce the residual strength and stiffness of a structure or result in unfavorable load paths. Emphasizing defect identification and restitution, Defects and Damage in Composite Materials and Structures explains how defects and damage in composite materials and structures impact composite component performance. Providing ready access to an extensive, descriptive list of defects and damage types, this must-have reference: Examines defect criticality in composite structures Recommends repair actions to restore structural integrity Discusses failure modes and mechanisms of composites due to defects Reviews NDI processes for finding and identifying defects in composite materials Relating defect detection methods to defect type, the author merges his experience in the field of in-service activities for composite airframe maintenance and repair with indispensable reports and articles on defects and damage in advanced composite materials from the last 50 years.

From a March 2001 symposium in Phoenix, Arizona, 17 papers consider such topics as tabbed versus untabbed fiber-reinforced composite compression, qualification using a nested experimental design, determining and characterizing imperfections in composite pressure vessels, philosophies for assessing t

Over much of the last three decades, the evolution of techniques for characterizing composite materials has struggled to keep up with the advances of composite materials themselves and their broadening areas of application. In recent years, however, much work has been done to consolidate test methods and better understand those being used. Finally,

Volume 1 of this six-volume compendium contains guidelines for determining the properties of polymer matrix composite material systems and their constituents, as well as the properties of generic structural elements, including test planning, test matrices, sampling, conditioning, test procedure selection, data reporting, data reduction, statistical analysis, and other related topics. Special attention is given to the statistical treatment and analysis of data. Volume 1 contains guidelines for general development of material characterization data as well as specific requirements for publication of material data in CMH-17. The Composite Materials Handbook, referred to by industry groups as CMH-17, is a six-volume engineering reference tool that contains over 1,000 records of the latest test data for polymer matrix, metal matrix, ceramic matrix, and structural sandwich composites. CMH-17 provides information and guidance necessary to design and fabricate end items from composite materials. It includes properties of composite materials that meet specific data requirements as well as guidelines for design, analysis, material selection, manufacturing, quality control, and repair. The primary purpose of the handbook is to standardize engineering methodologies related to testing, data reduction, and reporting of property data for current and emerging composite materials. It is used by engineers worldwide in designing and fabricating products made from composite materials.

Annotation In papers presented at the Tenth ASTM Conference on Composite Materials, held in San Francisco, April 1990, important composite materials technical issues are discussed in eight sections: compression test methodology analysis and development; general test methodology analysis and development; material mechanical properties and failure criteria; advanced materials analysis and test; analysis, test, and certification of structure; quality assurance and process control; interlaminar fracture analysis and test; and damage, flows, and repair. Member price, $95. Annotation copyrighted by Book News, Inc., Portland, OR.